    J. Michalicka, S. Li, Z. Bi, Y. Zhang, Ondrej Man, Y. Hong, Y. Wu, W. Ni, H. Fan, Günther Benstetter, L. Liu, Q. Yang, D. Liu

    The effect of O2 impurity on surface morphology of polycrystalline W during low-energy and high-flux He+ irradiation

    Fusion Engineering and Design, vol. 139, pp. 96-103

    2019

    DOI: 10.1016/j.fusengdes.2019.01.003

    Abstract anzeigen

    The interaction between the impurities (such as carbon, nitrogen, oxygen) and the plasma-facing materials (PFMs) can profoundly influence the performance and service of the PFMs. In this paper, we investigated the influence of oxygen (O2) impurity in the helium radio frequency (RF) plasma on the surface morphology of polycrystalline tungsten (W) irradiated at the surface temperature of 1450 ± 50 K and the ion energy of 100 eV. The pressure ratio of O2 to He (R) in RF source varied from 4.0 × 10−6 to 9.0 × 10-2. The total irradiation flux and fluence were ˜1.2 × 1022 ions·m-2·s-1 and ˜1.0 × 1026 ions·m-2, respectively. After He+ irradiation, the specimen surface morphology was observed by scanning electron microscopy. It was found that with increasing R from 4.0 × 10−6 to 9.0 × 10-2 the thickness of nano-fuzz layer at the W surface was thinner and thinner, accompanied by the formation of rod-like structures. The erosion yield increased from 5.2 × 10-4 to 2.3 × 10-2 W/ion when R varied from 4.0 × 10-6 to 9.0 × 10-2. The X-ray diffraction analysis shows that tungsten oxides were formed at the near surface of specimens when R exceeded 1.8 × 10-2. The erosion yield measurements revealed that in addition to surface physical sputtering process, the chemical erosion process could occur due to the interaction between oxygen-containing species and W at the surface. The results indicated that the presence of O2 impurity in He plasma can obviously affect the surface microstructure of W. The study suggested that O2 impurity can effectively reduce the growth of nano-fuzz structures.

    NachhaltigElektrotechnik und Medientechnik

    Zeitschriftenartikel

    S. Li, Z. Bi, Y. Zhang, D. Liu, Y. Hong, Y. Wu, W. Ni, H. Fan, Günther Benstetter, L. Liu, Q. Yang

    Surface damages of polycrystalline W and La2O3-doped W induced by high-flux He plasma irradiation

    Journal of Nuclear Materials, vol. 501, no. April, pp. 275-281

    2018

    Abstract anzeigen

    In this study, polycrystalline tungsten (W) and three oxide dispersed strengthened W with 0.1 vol %, 1.0 vol % and 5.0 vol % lanthanum trioxide (La2O3) were irradiated with low-energy (200 eV) and high-flux (5.8 × 1021 or 1.4 × 1022 ions/m2⋅s) He+ ions at elevated temperature. After He+ irradiation at a fluence of 3.0 × 1025/m2, their surface damages were observed by scanning electron microscopy, energy dispersive spectroscopy, scanning electron microscopy-electron backscatter diffraction, and conductive atomic force microscopy. Micron-sized holes were formed on the surface of W alloys after He+ irradiation at 1100 K. Analysis shows that the La2O3 grains doped in W were sputtered preferentially by the high-flux He+ ions when compared with the W grains. For irradiation at 1550 K, W nano-fuzz was formed at the surfaces of both polycrystalline W and La2O3-doped W. The thickness of the fuzz layers formed at the surface of La2O3-doped W is 40% lower than the one of polycrystalline W. The presence of La2O3 could suppress the diffusion and coalescence of He atoms inside W, which plays an important role in the growth of nanostructures fuzz.

    NachhaltigElektrotechnik und Medientechnik

    Zeitschriftenartikel

    D. Liu, W. Ni, H. Fan, Günther Benstetter, L. Liu, Q. Yang, Y. You, C. Liu

    Surface degeneration of W crystal irradiated with low-energy hydrogen ions

    Scientific Reports (Nature Publishing Group), vol. 6, no. Article number: 23738

    2016

    DOI: 10.1038/srep23738

    Abstract anzeigen

    The damage layer of a W (100) crystal irradiated with 120 eV hydrogen ions at a fluence of up to 1.5 × 1025/m2 was investigated by scanning electron microscopy and conductive atomic force microscopy (CAFM). The periodic surface degeneration of the W crystal at a surface temperature of 373 K was formed at increasing hydrogen fluence. Observations by CCD camera and CAFM indicate the existence of ultrathin surface layers due to low-energy H irradiation. The W surface layer can contain a high density of nanometer-sized defects, resulting in the thermal instability of W atoms in the surface layer. Our findings suggest that the periodic surface degeneration of the W crystal can be ascribed to the lateral erosion of W surface layers falling off during the low-energy hydrogen irradiation. Our density functional theory calculations confirm the thermal instability of W atoms in the top layer, especially if H atoms are adsorbed on the surface.

    NachhaltigElektrotechnik und Medientechnik

    Zeitschriftenartikel

    S. Li, Z. Bi, D. Liu, Y. Hong, W. Ni, H. Fan, Günther Benstetter, L. Liu, Q. Yang

    High-flux He+ irradiation effects on surface damages of tungsten under ITER relevant conditions

    Journal of Nuclear Materials, vol. 471, no. April, pp. 1-7

    2016

    DOI: 10.1016/j.jnucmat.2016.01.001

    Abstract anzeigen

    A large-power inductively coupled plasma source was designed to perform the continuous helium ions (He+) irradiations of polycrystalline tungsten (W) under International Thermonuclear Experimental Reactor (ITER) relevant conditions. He+ irradiations were performed at He+ fluxes of 2.3 × 1021–1.6 × 1022/m2 s and He+ energies of 12–220 eV. Surface damages and microstructures of irradiated W were observed by scanning electron microscopy. This study showed the growth of nano-fuzzes with their lengths of 1.3–2.0 μm at He+ energies of >70 eV or He+ fluxes of >1.3 × 1022/m2 s. Nanometer-sized defects or columnar microstructures were formed in W surface layer due to low-energy He+ irradiations at an elevated temperature (>1300 K). The diffusion and coalescence of He atoms in W surface layers led to the growth and structures of nano-fuzzes. This study indicated that a reduction of He+ energy below 12–30 eV may greatly decrease the surface damage of tungsten diverter in the fusion reactor.

    NachhaltigElektrotechnik und Medientechnik

    Zeitschriftenartikel

    D. Liu, C. Liu, W. Ni, Y. Wang, H. Fan, Günther Benstetter, Y.-W. You, L. Liu, Q. Yang

    Nanostructured fuzz growth on tungsten under low-energy and high-flux He irradiation

    Scientific Reports (Nature Publishing Group), vol. 5, no. Article number: 10959, pp. 1-9

    2015

    DOI: 10.1038/srep10959

    NachhaltigElektrotechnik und Medientechnik

    Zeitschriftenartikel

    D. Liu, Tobias Berthold, W. Ni, H. Fan, Günther Benstetter, L. Liu, Q. Yang

    Ordered arrangement of irradiation-induced defects of polycrystalline tungsten irradiated with low-energy hydrogen ions

    Journal of Nuclear Materials, vol. 464, pp. 216-220

    2015

    NachhaltigElektrotechnik und Medientechnik

    Zeitschriftenartikel

    D. Liu, Tobias Berthold, W. Ni, Y. Wang, H. Fan, Günther Benstetter, L. Liu, Q. Yang

    Observation of interstitial loops in He+ irradiated W by conductive atomic force microscopy

    Acta Materialia, vol. 92, pp. 178-188

    2015